Phase A | |
KSG-210 (Dimethicone PEG-10/15 crosspolymer (&) dimethicone) | 3.00 |
KSG-15 (Cyclopentasiloxane (&) dimethicone/vinyl dimethicone crosspolymer) | 2.00 |
KF-6028 (PEG-9 polydimethylsiloxyethyl dimethicone) | 1.00 |
KF-995 (Cyclopentasiloxane) | 5.00 |
DMF-A6 (Dimethicone) | 5.00 |
DMF-50CS (Dimethicone) | 2.00 |
Isotridecyl Isononanoate | 4.00 |
KP-545 (Cyclopentasiloxane (&) acrylates/dimethicone copolymer) | 2.50 |
KF-7312J (Cyclopentasiloxane (and) trimethylsiloxysilicate) | 2.50 |
SPD-T5 (Cyclopentasiloxane (&) titanium dioxide (&) polyglyceryl-3 polydimethylsiloxyethyl dimethicone (&) aluminum hydroxide (&) stearic acid) | 10.00 |
SPD-Z5 (Zinc oxide & cyclopentasiloxane & polyglyceryl-3 polydimethylsiloxyethyl dimethicone & triethoxysilylethyl polydimethylsiloxyethyl hexyl dimethicone) | 20.00 |
Phase B | |
Sodium citrate | 0.20 |
Sodium chloride | 1.00 |
Glycerin | 5.00 |
Water | 34.00 |
Phase C | |
KSP-100 (Vinyl dimethicone/methicone silsesquioxane crosspolymer) | 2.00 |
Phase D | |
Phenoxyethanol (&) caprylyl glycol | 0.80 |
Procedure | |
(500g): 1. Combine A and mix well using a dispersing blade. 2. Combine B and mix well. 3. Slowly add B to A and mix for ~10 minutes under moderate shear. 4. Add C and mix until uniform. 5. Add phase D and mix until uniform. | |
Properties | |
Total viscosity—Brookfield Heliopath RVT Spindle A Speed 5, 1 min @ 25°C = 5,000 CPS. FDA In-Vivo SPF-31, CWL 370nm, 80 min water resistance (n=10 subject). Room temperature/50°C 1 month/freeze thaw 3 cycles (-20°C/RT 3cycles)-stable. | |
More Information | |
Shin Etsu Silicones www.shinetsusilicones.com |